DIN1.4547 UNS S31254 Super Austenitic Stainless Steel
Similar Grade: DIN1.4547, UNS S31254 , F44
Shape: Round, Flat, Square.
Size Range:
| |
Diameter(mm) |
Thickness (mm) |
Width (mm) |
Length(mm) |
| Round |
50-420 |
- |
- |
2000-5800 |
| Square |
50-420 |
- |
- |
2000-5800 |
| flat |
- |
20-50 |
80-600 |
2000-5800 |
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
| Packing details |
In seaworthy packing, as your requirement. |
| Delivery details |
within 30-50 days |
Chemical Composition:
| Grade |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Mo |
Cu |
N |
| 1.4547 |
0.02 max |
0.7 max |
1.0
max |
0.030 max |
0.010 max |
19.5-
20.5 |
17.5-
18.5 |
6.0-7.0 |
0.50-
1.00 |
0.18-0.25 |
Heat Treatment:
Hardness(HB): 260max
Tensile Strength (Mpa): 650-850
Yield Strength (Mpa): 300-340
Elongation (%) (Long.): 35min
Impact Value (J) (Long.): 100min
Corrosion Resistance: 1.4547 Super Austenitic Stainless Steel offers higher resistance to abrasion, erosion and cavitation erosion than other austenitic stainless grades such as 316. F44 Super Austenitic Stainless Steel has excellent resistance to corrosion in sea water and concentrated halide environments, with good resistance to crevice corrosion in seawater.
Welding: 1.4547 Super Austenitic Stainless Steel is readily weldeable with welding procedures used for other austenitic stainless steel specifications. Welding should be carried out at the lowest heat possible as due to its austenite structure it can be prone to hot cracking.
Applications:
1.4547 Super Austenitic Stainless Steel is ideally suited for use in halide environments and widely used in the chemical, marine, oil and gas industries. Typical applications include pumps, valves, heat exchangers, flanges and manifolds.
Product Description:
Material to 1.4547 Super Austenitic Stainless Steel is described as a 6% Mo super austenitic stainless
steel. The steel combines moderate mechanical strength (typically over 300 MPa yield strength) and high ductility with excellent corrosion resistance in seawater and a variety of industrial environments. Typically the alloy has a PREn(Pitting Resistance Equivalent) of 42-44 which ensures that the resistance to pitting corrosion is high. In addition, the steel provides good resistance to crevice corrosion.
Ambient and subzero temperature notch ductility is very good. These attributes mean that this high molybdenum stainless steel can be used successfully as an alternative to 300 series austenitic stainless steels (such as type 316) in applications where higher mechanical strength and/or
enhanced resistance to pitting and crevice corrosion is required. This alloy possesses a lower yield strength than that of duplex stainless steel (and much lower than that of super duplex steel) and pitting resistance which is comparable to super duplex stainless steel (such as UNS S32760 / S32750).