Composition | Wt% | ZrO2+Y2O3%≥99.5 |
Specific density | g/cm 3 | >6.0 |
Hardness(HV) | HRA | >87 |
Thermal expansion Coefficient(20-400) | (10 -6 /K) | 9.6(20~400) |
Elastic modulis | GPa | 200~250 |
Fracture toughness | MPa.m 1/2 | 7-10 |
Bending strength | MPa | >1150 |
Grain size | μm | <0.6 |
Thermal conductivity | W/(m .k) | 2.5 |
Item No. | HB3HR21 | HB4HR21 | HB5HR21 | HB6HR21 | HBCHR21 |
Weight(g) | 39 | 48 | 96 | 111 | 115 |
Blade size(mm) | 73x20x1 | 113x29x1 | 133x48x1.5 | 163x48x1.5 | 148x50x1.5 |
Handle length(mm) | 107 | 107 | 127 | 127 | 127 |
Total length(mm) | 180 | 220 | 260 | 290 | 275 |