Shape: | Fiberglass Mesh |
---|---|
Fiber Characteristics: | E-Glass |
Diameter of Filaments: | Primary Fibers |
Fiber Appearance: | Continous Fiber |
Glass Composition: | E-Glass |
Heat Resistance Temperature: | H Grade(180) |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Banding tapes are of high quality, which consist of parallel twisted E- Glass yarns preimpregnated with a special thermosetting polyester resin.
Characters and Applications:
Class H(180 celsiuse degree) insulating material, high tensile strength, high resistance to shocks, high modulus of elasticity, dimensional stability. Widely used as ideal banding materials for electrical motors, transformers and lighting arresters.
Type:H200-W
Item | Unit | Specification | Test data | Test Condition |
Volatile Content(75ºC±2ºC/lh) | % | ≤2 | 1.22 | GB/T22471.2-2008 |
Resin Content | % | 27±2 | 28.8 | |
Soluble Resin Content(Toluen, ethanol = 3:2 solvent heat to 30 to 50ºC soaked 30 min, secondly soaked at this temperature for 15 min, then rinse with alcohol, roast 155ºC for 1h) | % | ≥90 | 95.2 | |
Settability(155ºC±2ºC/2h) | - | Easy to peel and not sticky | meet the requirement | |
Tensile Strength(Ring Test Speciment) Normalcy |
Mpa | ≥900 | 1445 | |
Tensile Strength(Ring Test Speciment) 200ºC±2ºC/30min |
Mpa | ≥560 | 879 | |
Tensile Modulus Of Elasticity(Ring Test Speciment) | Mpa | ≥4.5×104 | 8.46×104 |