Item | Type | PY Polyester G Glassfibre PYG Glassfibre enhance polyester felt PE PE Film S Sand M Mineral | ||||||
Grade | I | II | ||||||
Reinforcement | PY | G | PYG | |||||
Surface | PE | San | Mineral | |||||
Thickness | 2mm | 3mm | 4mm | 5mm | ||||
With | 1000mm |
No. | Item | |||||||||||||
PY | G | PY | G | PYG | ||||||||||
1 | Soluble content/(g/m ²)≥ | 3cm | 2100 | * | ||||||||||
4cm | 2900 | * | ||||||||||||
5cm | 3500 | |||||||||||||
Test | * | No flame | * | No flame | * | |||||||||
2 | Heat resistance | ºC | 90 | 105 | ||||||||||
≤mm | 2 | |||||||||||||
Test | No flow, no dripping | |||||||||||||
3 | Low temperature flexibility/ºC | -20 | -25 | |||||||||||
No crack | ||||||||||||||
4 | Impermeability 30 minutes | 0.3MPa | 0.2MPa | 0.3MPa | ||||||||||
5 | Tension | Maximum/(N/50mm) ≥ | 500 | 350 | 800 | 500 | 900 | |||||||
Secondly-Maximum | * | * | * | * | 800 | |||||||||
Test | No crack, no apart | |||||||||||||
6 | Elongation | Maximum/%≥ | 30 | * | 40 | * | * | |||||||
Secondly-Maximum≥ | * | * | 15 | |||||||||||
7 | Oil Leaking | Pieces≥ | 2 |
No. | Item | ||||||||||||||
PY | G | PY | G | PYG | |||||||||||
1 | Soluble content/(g/m²)≥ | 3cm | 2100 | * | |||||||||||
4cm | 2900 | * | |||||||||||||
5cm | 3500 | ||||||||||||||
Test | * | No flame | * | No flame | * | ||||||||||
2 | Heat resistance | ºC | 110 | 130 | |||||||||||
≤mm | 2 | ||||||||||||||
Test | No flow, no dripping | ||||||||||||||
3 | Low temperature flexibility/ºC | -7 | -15 | ||||||||||||
No crack | |||||||||||||||
4 | Impermeability 30 minutes | 0.3MPa | 0.2MPa | 0.3MPa | |||||||||||
5 | Tension | Maximum/(N/50mm) ≥ | 500 | 350 | 800 | 500 | 900 | ||||||||
Secondly-Maximum | * | * | * | * | 800 | ||||||||||
Test | No crack, no apart | ||||||||||||||
6 | Elongation | Maximum/%≥ | 30 | * | 40 | * | * | ||||||||
Secondly-Maximum≥ | * | * | 15 |