Feature: | Oxidative Degradable |
---|---|
CAS No.: | 32131-17-2 |
Formula: | (C12h22n2o2)N |
Samples: |
BAG
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
polyphthalamide (PPA) is heat stabilized cost effective solution for applications requiring stiffness
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | |||||||
AT-1116 HS polyphthalamide (PPA) is a toughened, heat stabilized 16% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional stability, chemical resistance and ductility. This resin has a high heat deflection temperature and a high flexural modulus, with greater tensile elongation than untoughened glass reinforced PPA.Features: Good Chemical Resistance; Good Dimensional Stability; Heat Stabilized; High Heat Resistance; Impact Modified Uses: Automotive Applications; Automotive Electronics; Automotive Under the Hood; Bearings; Bobbins; Connectors; General Purpose; Industrial Applications; Industrial Parts; Machine/Mechanical Parts; Metal ReplacementInjection Molding Notes: compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122° F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that resins be dried prior to molding. Automotive Specifications ASTM D4000 PPA0111 G17 KD124 KN055 PN046 YI238 LD002 Color: BK 324 Black; ASTM D4000 PPA0111 G17 KD124 KN055 PN046 YI238 LD002 Color: NT Natural; ASTM D6779 PA123G15 YI220; GM GMN6828 Color: BK 324 Black; GM GMN6828 Color: NT Natural; GM GMP.PPA.009 Color: BK 324 Black; GM GMP.PPA.009 Color: NT Natural; GM GMW15702-021991 Color: BK 324 Black; GM GMW15702-021991 Color: NT Natural; GM GMW16359P-PPA-GF15 Color: BK 324 Black; GM GMW16359P-PPA-GF15 Color: NT Natural; ISO 1874-PA 6T/6I/66-HI, MH, 12-060, GF16; YAZAKI YPES-25-02-305 Color: BK 324 Black; YAZAKI YPES-25-02-305 Color: NT NaturalInformation provided by Solvay Specialty Polymers. |
|||||||
General | |||||||
Form | Resin | Pellets | |||||
Filler | 16 % | Glass Fiber | |||||
UL Yellow Card | E95746-253246 | ||||||
Physical | Nominal Value | Test Method | |||||
Density / Specific Gravity | 1.28 g/cm³ | ISO 1183 | |||||
Filler Content(Glass Fiber) | 16 % | ||||||
Water Absorption(Time 24 hr) | 0.20 % | ISO 62 | |||||
Linear Mold Shrinkage, Flow | 0.6 % | ||||||
Linear Mold Shrinkage, Transverse | 0.6 % | ASTM D955 | |||||
Mechanical Nominal Value | Test Method | ||||||
Tensile Strength, Break Temperature; 100 °C Temperature; 23 °C |
65.5 MPa 160 MPa |
ISO 527-2 | |||||
Tensile Strength 161 MPa | ASTM D638 | ||||||
Elongation at Break | |||||||
3.8 % | ASTM D638 | ||||||
Temperature; 23 °C 3.7 % | ISO 527-2 | ||||||
Temperature; 100 °C 4.2 % | ISO 527-2 | ||||||
Tensile Modulus | |||||||
6480 MPa | ASTM D638 | ||||||
Temperature; 100 °C;2 mm/min 6690 MPa | ISO 527-2 | ||||||
Temperature; 23 °C;2 mm/min 6890 MPa | ISO 527-2 | ||||||
Flexural Strength | |||||||
226 MPa | ASTM D790 | ||||||
Temperature; 100 °C 141 MPa | ISO 178 | ||||||
Temperature; 23 °C 197 MPa | ISO 178 | ||||||
Flexural Modulus | |||||||
6000 MPa | ASTM D790 | ||||||
Temperature; 100 °C 4960 MPa | ISO 178 | ||||||
Temperature; 23 °C 6690 MPa | ISO 178 | ||||||
Compressive Strength 124 MPa | ASTM D695 | ||||||
Shear Strength 69.6 MPa | ASTM D732 | ||||||
Izod Impact, Notched(Temperature; 23 °C) 96 J/m | ASTM D256 | ||||||
Izod Impact, Unnotched(Temperature; 23 °C) 960 J/m | ASTM D256 | ||||||
Izod Impact, Notched, ISO(Temperature; 23 °C) 8.00 kJ/m² | ISO 180-1 | ||||||
Izod Impact, Unnotched, ISO(Temperature; 23 °C) 53.0 kJ/m² | ISO 180-1 | ||||||
C harpy Impact Unnotched(Temperature; 23 °C;Edgewise)86 kJ/m² | ISO 179/1 | ||||||
C harpy Impact, Notched(Temperature; 23 °C) 9 kJ/m² | ISO 179 | ||||||
Dart Drop, Total Energy 10.0 J | ASTM D3763 | ||||||
Thermal | Nominal Value | Test Method | |||||
CTE, Flow Temperature; 100 - 200 °C Temperature; 0 - 100 °C |
16.0 µm/m-°C 22.0 µm/m-°C |
ASTM E831;TMA |
|||||
CLTE, Transverse Temperature; 0 - 100 °C Temperature; 100 - 200 °C |
75.0 µm/m-°C 120 µm/m-°C |
ASTM E831;TMA |
|||||
Melting Point | 310 °C | ASTM D3418 | |||||
Deflection Temperature Pressure; 0.46 MPa;Annealed Pressure; 1.8 MPa;Annealed Pressure; 1.8 MPa |
268 °C 254 °C 258 °C |
ASTM D648 ASTM D648 ISO 75-2/A |
|||||
Processing | Nominal Value | ||||||
Rear Barrel Temperature | 304 - 318 °C | ||||||
Front Barrel Temperature | 316 - 329 °C | ||||||
Melt Temperature | 321 - 343 °C | ||||||
Mold Temperature | 135 °C | ||||||
Drying Temperature(Time 4 hr) | 110 °C | ||||||
Moisture Content | < = 0.045 % |