Feature: | Plastics |
---|---|
CAS No.: | 25766-59-0 |
Formula: | C6h4c(CH3)2c6h4oco2-]N |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | ||||
XD2322 polycarbonate (PC) copolymer resin is a UV stabilized opaque grade. This resin offers UL94 [email protected] flame retardancy based on non-bromine, non-chlorine FR system, excellent low temperature ductility characteristics and processability. XD2322 resin is an excellent candidate for a wide range of applications such as electronic vehicles (EV) and 5G devices. |
||||
General | ||||
Form | Resin Pellets | |||
Feature |
High Impact Non-Chlorinated |
Outdoor | Non-Brominated & Non- Chlorinated Flame Retardant |
|
Uses | Consumer Energy Storage |
Healthcare Electrical | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.19 1.19 g/cm³ |
ASTM D792 ISO 1183 |
||
Mold Shrinkage, Flow(3.2 mm) | 0.4 - 0.8 % | Method | ||
Mold Shrinkage, XFlow(3.2 mm) | 0.4 - 0.8 % | Method | ||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 16 g/10min | ASTM D1238 | ||
Water Absorption(23 °C;saturated) | 0.4 % | ISO 62-1 | ||
Moisture Absorption(23 °C;50% RH/Equilibrium) | 0.15 % | ISO 62-4 | ||
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 15 cm³/10 min | ISO 1133 | ||
UV light, water exposure/immersion | f1 | UL 746C | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Notched | ASTM D256 | |||
23 °C | 780 J/m | |||
-30 °C | 652 J/m | |||
-40 °C | 360 J/m | |||
Instrumented Dart Impact, Total Energy(23 °C) | 66 J | ASTM D3763 | ||
Unnotched Izod Impact Strength | ISO 180/1U | |||
unnotched;80*10*3;23 °C 0 | NB kJ/m² | |||
unnotched;80*10*3;-30 °C 0 | NB kJ/m² | |||
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 |
63 kJ/m² 29 kJ/m² |
ISO 180/1A | ||
Tensile Stress, Yield | ||||
50 mm/min;Type I | 58 MPa | ASTM D638 | ||
50 mm/min | 56 MPa | ISO 527 | ||
Tensile Stress, Break | ||||
50 mm/min;Type I | 59 MPa | ASTM D638 | ||
50 mm/min | 57 MPa | ISO 527 | ||
Tensile Strain, Yield | ||||
50 mm/min;Type I | 6 % | ASTM D638 | ||
50 mm/min | 6 % | ISO 527 | ||
Tensile Strain, Break | ||||
50 mm/min;Type I | 112 % | ASTM D638 | ||
50 mm/min | 108 % | ISO 527 | ||
Tensile Modulus | ||||
5 mm/min | 2100 MPa | ASTM D638 | ||
1 mm/min | 2000 MPa | ISO 527 | ||
Flexural Strength | ||||
1.3 mm/min;50 mm;span | 92 MPa | ASTM D790 | ||
2 mm/min | 87 MPa | ISO 178 | ||
Flexural Modulus | ||||
1.3 mm/min;50 mm;span | 2400 MPa | ASTM D790 | ||
2 mm/min | 2100 MPa | ISO 178 | ||
Thermal | Nominal Value | Test Method | ||
Glow Wire Flammability Index(1.5 mm) | 960 °C | IEC 60695-2-12 | ||
Glow Wire Ignition Temperature [GWIT](1.5 mm) | 825 °C | IEC 60695-2-13 | ||
UL Recognized ≥ 3 mm ≥ 1.5 mm |
5VA V-0 |
UL 94 | ||
Relative Temp Index, Elec | 125 °C | UL 746B | ||
Relative Temp Index, Mechanical with Impact | 115 °C | UL 746B | ||
Relative Temp Index, Mechanical without Impact | 125 °C | UL 746B | ||
Vicat Softening Temperature(Rate B/50) | 140 °C | ASTM D1525 | ||
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 123 °C | ASTM D648 | ||
HDT/Af(1.8) | 118 °C | ISO 75/Af | ||
CTE, Flow(-40 - 40 °C) | 6.1e-05 1/°C | ASTM E831 | ||
CTE, XFlow(-40 - 40 °C) | 6.2e-05 1/°C | ASTM E831 | ||
Electrical | Nominal Value | Test Method | ||
Comparative tracking index M | 150 V | IEC 60112 | ||
Comparative Tracking Index, CTI | PLC 3 | UL 746A | ||
High Amp Arc Ignition, HAI 3 mm 1.5 mm |
PLC 0 PLC 1 |
UL 746A | ||
Hot-wire Ignition, HWI 3 mm 1.5 mm |
PLC 2 PLC 3 |
UL 746A | ||
Processing | Nominal Value | |||
Drying Temperature<Injection> | 120 °C | |||
Drying Time<Injection> | 3 - 4 hrs | |||
Drying Time, Cumulative<Injection> | 48 hrs | |||
Maximum Moisture Content<Injection> | 0.02 % | |||
Melt Temperature<Injection> | 295 - 315 °C | |||
Nozzle Temperature<Injection> | 290 - 310 °C | |||
Front, Zone 3 Temperature<Injection> | 295 - 315 °C | |||
Middle, Zone 2 Temperature<Injection> | 280 - 305 °C | |||
Rear, Zone 1 Temperature<Injection> | 270 - 295 °C | |||
Mold Temperature<Injection> | 70 - 95 °C | |||
Back Pressure<Injection> | 0.3 - 0.7 MPa | |||
Screw Speed <Injection> | 40 - 70 rpm | |||
Shot To Cylinder Size<Injection> | 40 - 60 % | |||
Vent Depth <Injection> | 0.025 - 0.076 mm |