Feature: | Flame Retardant Modified |
---|---|
CAS No.: | 25038-54-4 |
Formula: | (-Hn(CH2)5co-)N |
Material: | Polyamide(Nylon 6.66)/PA |
Usage: | Engineering Plastics |
Plastic Properties After Heated: | Thermoplastic Plastics |
Suppliers with verified business licenses
Items | Standard | Condition | Unit | Typical Value |
Physical properties | Dry | |||
Density | ASTM D792 | / | - | 1.16 |
Shrinkage | ASTM D955 | Parallel | % | 0.9-1.1 |
Normal | % | 0.9-1.1 | ||
Water Absorption | ASTM D570 | 23ºC, H2O, 24hr | % | 1.55 |
Mechanical properties | Dry | |||
Tensile Strength at Break (3.2mm) | ASTM D638 | 50mm/min | MPa | 76 |
Elongation at Break (3.2mm) | ASTM D638 | 50mm/min | % | 15 |
Flexural Strength (3.2mm) | ASTM D790 | 5mm/min | MPa | 122 |
Flexural Modulus (3.2mm) | ASTM D790 | 5mm/min | MPa | 3292 |
Izod Impact Strength(6.4mm)(Notched) | ASTM D256 | 23ºC | J/m | 56 |
Rockwell Hardness | ASTM D785 | R scale | - | 120 |
Thermal properties | ||||
Melting Point | ASTM D1525 | 20ºC/min | ºC | 225 |
Heat Deflection Temperature | ASTM D648 | 1.8MPa | ºC | 75 |
Flammability(0.8mm) | UL94 | Class | V0 |