Color: | White |
---|---|
Application: | SLS 3D Printing |
Transport Package: | 20kg/Barrel |
Specification: | As requested |
Trademark: | Yuanchen |
Origin: | China |
Customization: |
---|
Suppliers with verified business licenses
General physical properties
|
S 3300PA
|
3400GF Glass
|
FS 3400CF
|
S 3250MF
|
FS 4100PA
|
Nylon powder
|
microbead composite nylon powder
|
Carbon fiber composite nylon powder
|
Mineral fiber composite nylon powder
|
Nylon 11 powder
|
|
Bulk Density
|
0.48 g/cm³
|
0.67 g/cm³
|
0.51 g/cm³
|
0.55 g/cm³
|
0.49 g/cm³
|
Workpiece density
|
0.95 g/cm³
|
1.26 g/cm³
|
1.08-1.10g/cm³
|
1.20 g/cm³
|
1.03 g/cm³
|
Color
|
White
|
Gray
|
Black
|
Light grey
|
White
|
Melting point
|
183°C
|
184°C
|
184°C
|
183°C
|
203°C
|
Heat distortion temperature(HDT) 1.8 MPa GB/T 1634.2-2004
|
83.5°C
|
88°C
|
72°C
|
129°C
|
49°C
|
Heat distortion temperature (HDT) 0.45 MPa GB/T 1634.2-2004
|
146.2°C
|
162°C
|
168 °C
|
171°C
|
150°C
|
Tensile Strength GB/T 1040.2-2006
|
46 MPa
|
44 MPa
|
65-70 MPa
|
51 MPa
|
49MPa
|
Tensile modulus GB/T 1040.2-2006
|
1602 MPa
|
3500 MPa
|
4700-6500 MPa
|
6130 MPa
|
1542 MPa
|
Elongation at break GB/T 1040.2-2006
|
36%
|
5%
|
3.0-4.0%
|
5%
|
58%
|
Bending strength GB/T 9341-2008
|
46.3 MPa
|
68 MPa
|
94-113 MPa
|
76 MPa
|
60MPa
|