| CAS No.: | 9002-88-4 |
|---|---|
| Formula: | (Cnh2)N |
| Material: | Polyolefin |
| Usage: | General Plastics, Engineering Plastics, Specialty Plastics, FTTH Drop Cable |
| Plastic Properties After Heated: | Thermoplastic Plastics |
| Plastic Forming Method: | Extrusion |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier | Type | Product | Application | |||||||||
| T-PO003 | 90ºCLow-smoke, halogen-free and flame retardant polyolefin compound for FTTH drop cable( bow-type drop cable for access network) |
Common sheath for flame retardant wires and cables which operation temperature is at 90 ºC,cable can pass IEC60332-1/-2 burning test. |
|||||||||
| Zone | Zone 1 | Zone 2 | Zone 3 | Zone 4 | Head | Die | |||||
| temperature ºC | 110 | 135 | 150 | 150 | 160 | 160 | |||||
| Item | Unit | T-PO003 | |||||||||
| Standard | Typical | ||||||||||
| Density | g/cm3 | 1.50±0.02 | 1.49 | ||||||||
| Hardness | Shore D | -- | 52 | ||||||||
| Tensile Strength | ≥MPa | 10.0 | 12.1 | ||||||||
| Elongation at Break | ≥ % | 160 | 180 | ||||||||
| Thermal Aging | ºC×h | 110×240 | |||||||||
| TS/EB Retention | ≥ % | 75/75 | 109/90 | ||||||||
| 90ºCx 1kg Hot Deformation |
≤ % | 20 | 10 | ||||||||
| Impact Brittleness Temperature | ≤ ºC | -40 | Pass | ||||||||
| Volume Resistivity, at 20ºC | ≥Ω.m | 1.0×1010 | 1.0×1012 | ||||||||
| Oxygen Index | ≥ | 32 | 35 | ||||||||
| Smoke Density Flaming |
≤ | 100 | 65 | ||||||||
| Non flaming | ≤ | 250 | 215 | ||||||||
| Acidity of gases evolved (pH) | ≥ | 4.3 | 5.9 | ||||||||
| Conductivity of gases evolved | ≤μs/mm | 10 | 1.0 | ||||||||
| Content of halogen acids | ≤ mg/g | 5 | 1.0 | ||||||||
| Toxicity Index | ≤ | 2.5 | 1.1 | ||||||||
| Thermal Impact Test | |||||||||||
| Condition 150ºC×1h | No cracking | Pass | |||||||||