| Product Type: | Strip |
|---|---|
| Material: | Ni-Cr-Fe |
| Carbon Content: | Low Carbon |
| Transport Package: | Wooden Cases |
| Specification: | SGS |
| Trademark: | TANKII |
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier Ni |
28.5~29.5 | Fe | Bal. | Co | 16.8~17.8 | Si | ≤0.3 |
| Mo | ≤0.2 | Cu | ≤0.2 | Cr | ≤0.2 | Mn | ≤0.5 |
| C | ≤0.03 | P | ≤0.02 | S | ≤0.02 |
Code of condition |
Condition | Wire | Strip |
| R | Soft | ≤585 | ≤570 |
| 1/4I | 1/4 Hard | 585~725 | 520~630 |
| 1/2I | 1/2 Hard | 655~795 | 590~700 |
| 3/4I | 3/4 Hard | 725~860 | 600~770 |
| I | Hard | ≥850 | ≥700 |
Density (g/cm3) |
8.2 |
| Electrical resistivity at 20ºC(mm2/m) | 0.48 |
| Temperature factor of resistivity(20ºC~100ºC)X10-5/ºC | 3.7~3.9 |
| Curie point Tc/ ºC | 430 |
| Elastic Modulus, E/ Gpa | 138 |
| θ/ºC | α1/10-6ºC-1 | θ/ºC | α1/10-6ºC-1 |
| 20~60 | 7.8 | 20~500 | 6.2 |
| 20~100 | 6.4 | 20~550 | 7.1 |
| 20~200 | 5.9 | 20~600 | 7.8 |
| 20~300 | 5.3 | 20~700 | 9.2 |
| 20~400 | 5.1 | 20~800 | 10.2 |
| 20~450 | 5.3 | 20~900 | 11.4 |
| θ/ºC | 100 | 200 | 300 | 400 | 500 |
| λ/ W/(m*ºC) | 20.6 | 21.5 | 22.7 | 23.7 | 25.4 |
| The heat treatment process | |
| Annealing for stress relief | Heated to 470~540ºC and hold 1~2 h. Cold down |
| annealing | In vacuum heated to 750~900ºC |
| Holding time | 14 min~1h. |
| Cooling rate | No more than 10 ºC/min cooled to 200 ºC |
| Alloys Name | Type | Dimension | ||
| Alloy-4J29 | Wire | D= 0.1~8mm | ||
| Alloy-4J29 | Strip | W= 5~250mm | T= 0.1mm | |
| Alloy-4J29 | Foil | W= 10~100mm | T= 0.01~0.1 | |
| Alloy-4J29 | Bar | Dia= 8~100mm | L= 50~1000 | |