Product Description | ||||
Very high impact ABS. Toughness/rigidity. Good fatigue resistance. | ||||
General | ||||
Form | ||||
Feature | ||||
UL Yellow Card E207780-228354 | ||||
Appliances Electronic Displays Automotive Interior |
Lighting Applications Lawn And Garden Equipment Constraction |
Automotive Lighting Textile Applications Automotive Outdoor |
||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.05 g/cm³ | ASTM D792 | ||
Melt Mass-Flow Rate, MFR 230 °C;3.8 kg 220 °C;10 kg |
3.7 g/10min 15 g/10min |
ASTM D1238 ISO 1133 |
||
Molding Shrinkage, Flow(3.2 mm) | 0.50 - 0.80 % | Internal Method | ||
Melt Viscosity(240 °C;1.0e+3 sec^-1) | 245 Pa · s | ASTM D3835 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Modulus(5 mm/min) | 2270 MPa | ASTM D638 | ||
Tensile Strength, Yield(5 mm/min;Type I) | 44.0 MPa | ASTM D638 | ||
Tensile Strength, Break(5 mm/min;Type I) | 33.0 MPa | ASTM D638 | ||
Tensile Elongation, Yield(5 mm/min;Type I) | 2.1 % | ASTM D638 | ||
Tensile Elongation, Break(5 mm/min;Type I) | 26 % | ASTM D638 | ||
Flexural Modulus(1.3 mm/min;50 mm;Span) | 2340 MPa | ASTM D790 | ||
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) | 72.0 MPa | ASTM D790 | ||
Notched Izod Impact(23 °C) | 370 J/m | ASTM D256 | ||
Instrumented Dart Impact, Total Energy(23 °C) | 31.0 J | ASTM D3763 |
Product Description | ||||
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
General | ||||
Form | Resin | Pellets | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | |||
Water Absorption | 0.21 % | ASTM D570 | ||
Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
Linear Mold Shrinkage | 2.2 % | |||
Linear Mold Shrinkage, Transverse | 1.8 % | |||
Hardness, Rockwell R | 111 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
Elongation at Break | 30 % | ASTM D638 | ||
Flexural Strength | 52.0 MPa | ASTM D790 | ||
Flexural Modulus | 2100 MPa | ASTM D790 | ||
Compressive Strength | 66.0 MPa | ASTM D695 | ||
Shear Strength | 40.0 MPa | ASTM D732 | ||
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C |
50 J/m 30 J/m |
ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
152 °C 106 °C |
ASTM D648 | ||
Flammability, UL94 | HB | UL 94 |