| Material: | Polyester /Nylon with Rubber |
|---|---|
| Applications: | Rubber Hose ; Tyre ; Conveyor Belt |
| Type: | Rubberized |
| Style: | Rubber Coated |
| Pattern: | Plain |
| Width: | as Costomer′s Requirement |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier | No. | Item | Unit | 1870dtex/2 (1680D/2) |
1400dtex/2 (1260D/2) |
930dtex/2 (840D/2) |
2100dtex/2 (1890d/2) |
1170dtex/1 (1050D/1) |
700dtex/1 (630D/1) |
1870dtex/1 (1680D/1) |
1400dtex/1 (1260D/1) |
930dtex/1 (840D/1) |
| 1 | Breaking strength (min) | N/end | 279.3 | 215.6 | 137.2 | 313.6 | 90 | 50 | 137 | 107 | 70 |
| 2 | Elongation at 88.2N | % | 9.5±0.5 | - | - | 9.5±0.5 | - | - | 8.0±0.8 | - | - |
| Elongation at 66.6N | % | - | 9.5±0.5 | - | - | 8.0±0.8 | - | - | 7.0±0.8 | - | |
| Elongation at 44.1N | % | - | - | 9.5±0.5 | - | - | 7.5±0.8 | - | - | 7.5±0.8 | |
| 3 | Adhesive strength (min) | N/cm | 166.6 | 147 | 117.6 | 176.4 | 65 | 43 | 83 | 69 | 54 |
| 4 | Breaking strength difference (max) | % | 3.8 | 3.8 | 3.8 | 3.8 | 5 | 5 | 5 | 5 | 5 |
| 5 | Breaking elongation difference (max) | 6.3 | 6.3 | 6.3 | 6.3 | 7 | 7.5 | 7 | 7 | 7 | |
| 6 | Dip pick up | 4.5±1.0 | 4.5±1.0 | 4.5±1.0 | 4.5±1.00 | 4.2±0.8 | 4.2±1.00 | 4.2±1.00 | 4.2±1.00 | 4.2±1.00 | |
| 7 | Breaking elongation difference (max) | % | 23.0±2.0 | 23.0±2.0 | 22.0±2.0 | 23±2.0 | 20.0±2.0 | 19.0±2.0 | 20.0±2.0 | 20.0±2.0 | 20.0±2.0 |
| 8 | Diameter | mm | 0.78±0.03 | 0.65±0.03 | 0.55±0.03 | 0.78±0.03 | - | 0.23±0.03 | 0.5±0.03 | 0.43±0.03 | 0.32±0.03 |
| 9 | Primary twist(Z) | T/10cm | 32±15 | 37±15 | 46±15 | 32±15 | TPM/m: 20±15 | TPM/m: 26±15 | 16±10 | 19±10 | 21±15 |
| Second twist(S) | 32±15 | 37±15 | 46±15 | 32±15 | |||||||
| 10 | Heat shrinkage (max) | % | 6 | 6 | 6 | 4 | 4.5 | 4 | 4 | 4 | 4 |
| 11 | Moisture (max) | % | 1 | 1 | 1 | 1 | 0.8 | 0.8 | 0.8 | 0.8 | 0.8 |
| No. | Item | Unit | 1870dtex/2 (1680D/2) |
1400dtex/2 (1260D/2) |
930dtex/2 (840D/2) |
2100dtex/2 (1890d/2) |
1170dtex/1 (1050D/1) |
700dtex/1 (630D/1) |
1870dtex/1 (1680D/1) |
1400dtex/1 (1260D/1) |
930dtex/1 (840D/1) |
| 1 | Breaking strength (min) | N/end | 279.3 | 215.6 | 137.2 | 313.6 | 90 | 50 | 137 | 107 | 70 |
| 2 | Elongation at 88.2N | % | 9.5±0.5 | - | - | 9.5±0.5 | - | - | 8.0±0.8 | - | - |
| Elongation at 66.6N | % | - | 9.5±0.5 | - | - | 8.0±0.8 | - | - | 7.0±0.8 | - | |
| Elongation at 44.1N | % | - | - | 9.5±0.5 | - | - | 7.5±0.8 | - | - | 7.5±0.8 | |
| 3 | Adhesive strength (min) | N/cm | 166.6 | 147 | 117.6 | 176.4 | 65 | 43 | 83 | 69 | 54 |
| 4 | Breaking strength difference (max) | % | 3.8 | 3.8 | 3.8 | 3.8 | 5 | 5 | 5 | 5 | 5 |
| 5 | Breaking elongation difference (max) | 6.3 | 6.3 | 6.3 | 6.3 | 7 | 7.5 | 7 | 7 | 7 | |
| 6 | Dip pick up | 4.5±1.0 | 4.5±1.0 | 4.5±1.0 | 4.5±1.00 | 4.2±0.8 | 4.2±1.00 | 4.2±1.00 | 4.2±1.00 | 4.2±1.00 | |
| 7 | Breaking elongation difference (max) | % | 23.0±2.0 | 23.0±2.0 | 22.0±2.0 | 23±2.0 | 20.0±2.0 | 19.0±2.0 | 20.0±2.0 | 20.0±2.0 | 20.0±2.0 |
| 8 | Diameter | mm | 0.78±0.03 | 0.65±0.03 | 0.55±0.03 | 0.78±0.03 | - | 0.23±0.03 | 0.5±0.03 | 0.43±0.03 | 0.32±0.03 |
| 9 | Primary twist(Z) | T/10cm | 32±15 | 37±15 | 46±15 | 32±15 | TPM/m: 20±15 | TPM/m: 26±15 | 16±10 | 19±10 | 21±15 |
| Second twist(S) | 32±15 | 37±15 | 46±15 | 32±15 | |||||||
| 10 | Heat shrinkage (max) | % | 6 | 6 | 6 | 4 | 4.5 | 4 | 4 | 4 | 4 |
| 11 | Moisture (max) | % | 1 | 1 | 1 | 1 | 0.8 | 0.8 | 0.8 | 0.8 | 0.8 |