Feature: | Plastics |
---|---|
CAS No.: | 9003-56-9 |
Formula: | C45h51n3X2 |
Samples: |
25kg/bag
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | ||||
Features: Good Flow; 1.5mm V-2; 2.5mm V-0; 2.5mm 5VB; 3.0mm 5VA (TBBA series) Applications: Displays; Chassis; Modems; Power Panels; Power Outlets; Car Batteries; Cash Register Housings ; printer enclosures; remote controls; light boxes; fax machines; projectors; large MFPs; coffee makers; TV front and rear frames and car audio consoles Impact Resistant | ||||
General | ||||
Form | ||||
Feature | Excellent Processability Medium Impact Resistance | |||
UL Yellow Card E56070-565070 | ||||
Uses |
Batteries Light Covers Facsimile machine parts Printer Chassis |
Displays Printer Parts Projector Housing Audio Speaker Components |
Housing Panel Socket Remote Controls Coffee Machine |
|
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity(23 °C) | 1.16 g/cm³ | ISO 1183 | ||
Melt Volume-Flow Rate, MVR(220 °C;10 kg) | 44 cm³/10 min | ISO 1133 | ||
Molding Shrinkage | 0.30 - 0.60 % | ISO 294-4 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield(50 mm/min) | 39.0 MPa | ISO 527-2/50 | ||
Tensile Strength, Break(50 mm/min) | 30.0 MPa | ISO 527-2/50 | ||
Tensile Elongation, Break(50 mm/min) | 10 % | ISO 527-2/50 | ||
Flexural Modulus(2 mm/min) | 1800 MPa | ISO 178 | ||
Flexural Strength(2 mm/min) | 57.0 MPa | ISO 178 | ||
Charpy Notched Impact Strength -30 °C 23 °C |
11 kJ/m² 25 kJ/m² |
ISO 179 | ||
Notched Izod Impact -30 °C 23 °C |
11 kJ/m² 24 kJ/m² |
ISO 180/1A |
Thermal | Nominal Value | Test Method | |
Deflection Temperature Under Load, Unannealed(1.8 MPa) | 77.0 °C | ISO 75-2/A | |
Deflection Temperature Under Load, Annealed(1.8 | MPa) 85.0 °C | ISO 75-2/A | |
Vicat Softening Temperature | |||
5 kg;50 ºC/hr | 80.0 °C | ISO 306/B50 | |
50 ºC/hr;1 kg | 94.0 °C | ISO 306/A50 | |
CLTE, Flow | 8.55E-5 | ISO 11359-2 | |
Flame Rating 1.5 mm 2.5 mm 2.5 mm 3 mm |
V-2 V-0 5VB 5VA |
UL 94 | |
Processing | Nominal Value | ||
Drying Temperature<Injection> | 80 - 85 °C | ||
Drying Time<Injection> | 2.0 - 4.0 hr | ||
Rear Temperature<Injection> | 180 - 210 °C | ||
Middle Temperature<injection> | 190 - 220 °C | ||
Front Temperature<Injection> | 190 - 220 °C | ||
Mold Temperature<Injection> | 40 - 70 °C | ||
Injection Rate<Injection> | Slow-Moderate | ||
Back Pressure<Injection> | 0.5 - 1 MPa | ||
Injection Pressure<Injection> | 50 - 60 % | ||
Holding Pressure<Injection> | 40 - 50 % |