Audited Supplier PA66 glass fibre reinforced injection moulding grade with good dimensional stability
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| Product Description | |||||
| An impact-modified, glassfibre reinforced injection moulding grade with good dimensional stability. | |||||
| General | |||||
| Form | Resin Pellets | ||||
| Filler | 30 % Glass Fiber | ||||
| Feature | Good Dimensional Ec 1907/2006 (Reach) |
High Impact | Fuel Resistant | ||
| UL Yellow Card | E41871-233758 | ||||
| Physical | Nominal Value | Test Method | |||
| Density, dry | 1.33 g/cm³ | ISO 1183 | |||
| Dry: Apparent Density, Bulk | 0.70 g/cm³ | No Standard | |||
| Dry: Melt Volume-Flow Rate, MVR(275 °C;5 kg) | 15 cm³/10 min | ISO 1133 | |||
| Dry: Water Absorption, Saturation(23 °C) | 4.7 - 5.3 % | ISO 62 | |||
| Dry: Water Absorption, Equilibrium(50% RH;23 °C) | 1.3 - 1.7 % | ISO 62 | |||
| Dry: Viscosity Number, (96% H2SO4) | 160 cm³/g | ISO 307 | |||
| Dry: Mold Shrinkage, Constrained(TW = 80 °C;107*47*1;5 mm;TM = 290 °C) | 0.55 % | ||||
| Mechanical | Nominal Value | Test Method | |||
| Dry: Tensile Modulus | 8500 MPa | ISO 527-2 | |||
| Condition: Tensile Modulus | 6000 MPa | ISO 527-2 | |||
| Dry: Tensile Stress, Break | 140 MPa | ISO 527-2 | |||
| Condition: Tensile Stress, Break | 100 MPa | ISO 527-2 | |||
| Dry: Tensile Strain, Break | 3.5 % | ISO 527-2 | |||
| Condition: Tensile Strain, Break | 6.0 % | ISO 527-2 | |||
| Condition: Tensile creep modulus(1.0e+3 hr;23 °C;strain < = 0.5%) | 3000 MPa | ISO 899-1 | |||
| Dry: Flexural Modulus | 7300 MPa | ISO 178 | |||
| Condition: Flexural Modulus | 4900 MPa | ISO 178 | |||
| Dry: Flexural Stress | 210 MPa | ISO 178 | |||
| Condition: Flexural Stress | 150 MPa | ISO 178 | |||
| Dry: Charpy Notched Impact Strength -30 °C 23 °C |
10 kJ/m² 19 kJ/m² |
ISO 179 1eA | |||
| Condition: Charpy Notched Impact Strength(23 °C) | 26 kJ/m² | ISO 179 1eA | |||
| Dry: Charpy Unnotched Impact Strength -30 °C 23 °C |
85 kJ/m² 90 kJ/m² |
ISO 179 1eU | |||
| Condition: Charpy Unnotched Impact Strength(23 °C) | 95 kJ/m² | ISO 179 1eU | |||
| Dry: Notched Izod Impact Strength -30 °C 23 °C |
15 kJ/m² 17 kJ/m² |
ISO 180/1A | |||
| Notched Izod Impact Strength: condition -30 °C 23 °C |
18 kJ/m² 20 kJ/m² |
ISO 180/1A | |||
| Thermal | Nominal Value | Test Method | |||
| Dry: Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
250 °C 240 °C |
ISO 75-2/B ISO 75-2/A |
|||
| Dry: Melting Temperature | 260 °C | ISO 11357-3 | |||
| Dry: CLTE, Flow(23 - 80 °C) | 2.5E-5 - 3.5E-5 cm/cm/°C | ISO 11359-2 | |||
| Dry: CLTE, Transverse(23 - 80 °C) | 6.0E-5 - 7.0E-5 cm/cm/°C | ISO 11359-2 | |||
| Dry: Specific Heat | 1700 J/kg/°C | No Standard | |||
| Dry: Thermal Conductivity | 0.35 W/m-K | DIN 52612 | |||
| Dry: Maximum Service Temperature - short cycle operation | 220 °C | ||||
| Dry: Flammability Classification(1.6 mm) | HB | ||||
| Electrical | Nominal Value | Test Method | |||
| Condition: Surface resistivity | 1.0E+10 ohms | IEC 60093 | |||
| Dry: Volume Resistivity | 1.0e+15 ohms ·cm | IEC 60093 | |||
| Condition: Volume resistivity | 1.0E+12 ohms ·cm | IEC 60093 | |||
| Dry: Relative permittivity(1.0e+6 Hz) | 3.50 | IEC 60250 | |||
| Condition: Relative Permittivity(1.0e+6 Hz) | 5.50 | IEC 60250 | |||
| Dry: Dissipation Factor(1.0e+6 Hz) | 0.014 | IEC 60250 | |||
| Condition: Dissipation factor(1.0e+6 Hz) | 0.16 | IEC 60250 | |||
| Dry: Comparative Tracking Index, Solution A | 550 V | IEC 60112 | |||
| Processing | Nominal Value | ||||
| Drying Temperature<Injection> | 80 °C | ||||
| Drying Time<Injection> | 4.0 hr | ||||
| Suggested Max Moisture<Injection> | 0.15 % | ||||
| Hopper Temperature<Injection> | 80 °C | ||||
| Rear Temperature<Injection> | 290 °C | ||||
| Middle Temperature<injection> | 290 °C | ||||
| Front Temperature<Injection> | 290 °C | ||||
| Nozzle Temperature<Injection> | 290 °C | ||||
| Processing Temp, Melt<Injection> | 280 - 300 °C | ||||
| Mold Temperature<Injection> | 80 - 90 °C | ||||
| Residence Time<Injection> | < 10.0 min | ||||
| Screw Speed <Injection> | < 18 m/min | ||||