| CAS No.: | 70131-67-8 |
|---|---|
| Formula: | Ho[(CH3)2sio]Nh |
| EINECS: | 000000 |
| Appearance: | Liquid |
| Usage: | Oil Drilling Auxiliary Agent, Water Treatment Chemicals, Rubber Auxiliary Agents, Plastic Auxiliary Agents, Coating Auxiliary Agents, Textile Auxiliary Agents, Paper Chemicals, Surfactants, Leather Auxiliary Agents, Electronics Chemicals |
| Color: | White |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier 
Hydroxyl silicone oil is made of polymerization of siloxane monomers, the molecular silicone materials have hydroxyl groups at both ends. The structural formula is as below:
HO-Si (CH3) 2 O [Si (CH3) 2 O] n Si(CH3)2-OH
Chemical name is a, w- dihydroxy polydimethylsiloxane, it's named 107 silicone rubber when the viscosity is above 2500mPa.S. In addition to the general performance of methyl silicone oil, it also has reactive hydroxyl groups, it can be made available some new material or crosslinked into elastomers (or membrane) .
Colorless transparent liquid with excellent electrical insulating properties and resistance to high temperature, high flash point, low freezing point, long-term used -50 o C ~ +250 o C conditions, low the viscosity-temperature coefficient, high compression ratio, low surface tension, hydrophobic moisture resistance, chemical inertness, physiologically inertness.
| Appearance | colorless transparent liquid |
| Viscosity (25oC, mpa.s) | 25~100000 (can be customized according to user requirements ) |
| Hydroxyl content (%) | 0.5 - 3 (related to the viscosity) |
Dosage:
Usually with the curing agent to achieve the crosslinking, it must be fixed by means of a coupling agent for the release paper, generally the curing agent is about 3 to 5% of gum base, the coupling agent is about 0.5 to 1 % of gum base.
In most cases the solvent was diluted with 10 times the first gum base, then add the coupling agent and the curing agent after mixing uniformly coated on the substrate surface at room temperature or heat curing. It need over 30 minutes at room temperature, and 30 seconds for 120 ~ 150 o C. there is no need any solvents for sealants and molds for rubber, add the curing agent and stir ( one-component and two-component curing agent is used is not the same ) , after 30 to 120 minutes degassing it can be cured .
1. The product should be stored in airtight plastic bucket clean not in contact with acid, alkali substances;
2. Stored at room temperature and ventilated shade;
3. According to the non -toxic and non-dangerous goods storage and transportation.