Product Description | ||
Extrusion molding grade, Light diffusion grade, Weather resistance, Flame resistance | ||
General | ||
Form Resin Pellets | ||
Feature Outdoor Diffusive | ||
UL Yellow Card E244324-103158490 | ||
Uses Lighting Applications Lighting Diffusers Led | ||
Physical Nominal Value Test Method | ||
Density / Specific Gravity 1.20 g/cm³ ISO 1183 | ||
Melt Volume-Flow Rate, MVR(300 °C;1.2 kg) 2.5 cm³/10 min ISO 1133 | ||
Molding Shrinkage, Across Flow(4 mm) 0.50 - 0.70 % Internal Method | ||
Molding Shrinkage, Flow(4 mm) 0.50 - 0.70 % Internal Method | ||
Water Absorption(24 hr;23 °C) 0.20 % ISO 62 | ||
Mechanical Nominal Value Test Method | ||
Tensile Modulus 2400 MPa ISO 527-2/1 | ||
Tensile Stress, Yield 64.0 MPa ISO 527-2/50 | ||
Tensile Stress, Break 50.0 MPa ISO 527-2/50 | ||
Tensile Strain, Yield 6.0 % ISO 527-2/50 | ||
Nominal Tensile Strain at Break 30 % ISO 527-2/50 | ||
Flexural Modulus(2 mm/min) 2140 MPa ISO 178 | ||
Flexural Stress(2 mm/min) 98.0 MPa ISO 178 | ||
C harpy Notched Impact Strength(23 °C) 13 kJ/m² ISO 179 | ||
C harpy Unnotched Impact Strength(23 °C) No Break ISO 179 | ||
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed(1.8 MPa) | 127 °C | ISO 75-2/A |
CLTE, Flow | 7.0E-5 cm/cm/°C | ISO 11359-2 |
CLTE, Transverse | 7.0E-5 cm/cm/°C | ISO 11359-2 |
RTI Elec(1.5 mm) | 130 °C | UL 746 |
RTI Imp(1.5 mm) | 125 °C | UL 746 |
RTI Str(1.5 mm) | 130 °C | UL 746 |
Flame Rating 0.8 mm 1 mm 2 mm |
V-0 V-0 5VB |
UL 94 |
Glow Wire Flammability Index 1 mm 3 mm |
930 °C 960 °C |
IEC 60695-2-12 |
Glow Wire Ignition Temperature [GWIT] 1 mm 3 mm |
850 °C 850 °C |
IEC 60695-2-13 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | > 1.0E+15 Ohms | IEC 60093 |
Volume Resistivity | > 1.0E+15 Ohms ·cm | IEC 60093 |
Optical | Nominal Value | Test Method |
Transmittance (3.0e+3 µm) | 47.0 % | ASTM D1003 |